BOROFLOAT®: SCHOTT 33 Borosilicate Glass | ||
---|---|---|
Glass Code: Schott |
Borofloat® 33 |
|
Type |
Borosilicate |
|
Color |
Clear |
|
Principal Use |
Industrial |
|
Thermal Expansion Multiply by 10-7 cm/cm/°C |
0 -300°C |
32.5 |
Maximum Operating Tempature °C |
Short Term < 10 Hours |
500 |
Long Term > 10 Hours |
450 |
|
Thermal Shock Resistance (20x20 cm2) data is Approximately |
< 3.8mm Thick |
175K |
5.0 - 5.5mm Thick |
160K |
|
6.5 - 150mm Thick |
150K |
|
Viscosity Data (This data is subject to normal manufacturing variations.) |
Strain Point °C |
518 |
Annealing Point °C |
560 |
|
Softening Point °C |
820 |
|
Working Point °C |
1270 |
|
Density q/cm3 |
2.2 |
|
Young's Modulus (64 Kn/mm2) |
64 |
|
Poisson's Ratio |
0.2 |
|
Refractive Index |
435.8 nm |
1.480 |
546.1nm |
1.473 |
|
589.3 nm |
1.471 |
|
1.469 |
||
Stress-Optical Coefficient, in MPa-1 K |
4.0 x 1 |